LOCTITE UK U-10FL
Description
urethane adhesive. Once mixed, the two-component urethane
cures at room temperature to form an ultra-clear, highly flexible
bond line, which provides excellent peel strength.
Ideal for bonding polycarbonate, and a variety of other plastics,
as well as glass, and metal. Suited for applications requiring a
clear, non-yellowing bond line.
The graph below shows the shear strength developed over time
on abraded, acid etched aluminum lap shears with an average
bondline gap of 3 to 9 mils and tested according to ASTM D1002.
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Material Safety Data Sheet, (MSDS).
Product shall be ideally stored in a cool, dry location in
unopened containers at a temperature between 8C to 28C
(46F to 82F) unless otherwise labeled. Optimal storage is at
the lower half of this temperature range. To prevent
contamination of unused product, do not return any material to
its original container. For further specific shelf life information,
contact your local Technical Service Center.
The data contained herein may be reported as a typical value
and/or range. Values are based on actual test data and are
verified on a periodic basis.
Read More
Read Less
LOCTITE UK U-10FL
- Shear Strength, Etched Aluminum : 1850 psi
- Key Substrates : Glass, Metal, Plastic, Polycarbonate
- Colour : Clear: Ultra Clear
- Cure Type : Two Component Mix
- Ultra-clear, non-yellowing
- Highly flexible bondline
- Excellent peel strength
- Room temperature cure
- Low viscosity
- Industrial grade
urethane adhesive. Once mixed, the two-component urethane
cures at room temperature to form an ultra-clear, highly flexible
bond line, which provides excellent peel strength.
TYPICAL APPLICATIONS
Ideal for bonding polycarbonate, and a variety of other plastics,
as well as glass, and metal. Suited for applications requiring a
clear, non-yellowing bond line.
TYPICAL CURING PERFORMANCE
Cure speed
The graph below shows the shear strength developed over time
on abraded, acid etched aluminum lap shears with an average
bondline gap of 3 to 9 mils and tested according to ASTM D1002.
GENERAL INFORMATION
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Material Safety Data Sheet, (MSDS).
Directions for use
- For high strength structural bonds, removal of surface
contaminates such as paint, oxide films, oils, dust, mold
release agents and all other surface contaminates. - Use gloves to minimize skin contact. DO NOT use solvents
for cleaning hands. - Dual Cartridges: To use simply insert the cartridge into the
application gun and start the plunger into the cylinders using
light pressure on the trigger. Next, remove the cartridge cap
and expel a small amount of adhesive to be sure both sides
are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end
of the cartridge and begin dispensing the adhesive. For
hand mixing, expel the desired amount of the adhesive and
mix thoroughly. Mix approximately 15 seconds after uniform
color is obtained. Bulk Containers: Mix thoroughly by
weight or volume in the proportions specified in Properties
of Uncured Material section. Mix vigorously approximately
15 seconds after uniform color is obtained. - For maximum bond strength, apply adhesive evenly to both
surfaces to be joined. - Application to the substrates should be made within 10
minutes. Larger quantities and/or higher temperatures will
reduce this working time. - Join the adhesive coated surfaces and allow to cure at 25C
(77F) for 24 hours for high strength. Heat up to 93C
(200F), will speed curing. - Keep parts from moving during cure. Contact pressure is
necessary. Maximum shear strength is obtained with a 3-9
mil bond line. - Excess uncured adhesive can be cleaned up with ketone
type solvents.
Storage
Product shall be ideally stored in a cool, dry location in
unopened containers at a temperature between 8C to 28C
(46F to 82F) unless otherwise labeled. Optimal storage is at
the lower half of this temperature range. To prevent
contamination of unused product, do not return any material to
its original container. For further specific shelf life information,
contact your local Technical Service Center.
Data Ranges
The data contained herein may be reported as a typical value
and/or range. Values are based on actual test data and are
verified on a periodic basis.
LOCTITE UK U-10FL
Sale price$0.00
Regular price (/)
Products dan Adhesive / Sealant
Categories
Loctite
Products Brand