LOCTITE UK U-10FL

  • Shear Strength, Etched Aluminum : 1850 psi
  • Key Substrates : Glass, Metal, Plastic, Polycarbonate
  • Colour : Clear: Ultra Clear
  • Cure Type : Two Component Mix
LOCTITE® UK U-10LV is an ultra-clear, 2-part, low viscosity urethane adhesive liquid that creates a non-yellowing, highly flexible bondline with excellent peel strength. This industrial grade product cures at room temperature and is ideal for bonding polycarbonate and many other plastics, as well as glass and metal.
  • Ultra-clear, non-yellowing
  • Highly flexible bondline
  • Excellent peel strength
  • Room temperature cure
  • Low viscosity
  • Industrial grade
LOCTITE® UK U-10FL is a low-viscosity, industrial grade
urethane adhesive. Once mixed, the two-component urethane
cures at room temperature to form an ultra-clear, highly flexible
bond line, which provides excellent peel strength.
TYPICAL APPLICATIONS

Ideal for bonding polycarbonate, and a variety of other plastics,
as well as glass, and metal. Suited for applications requiring a
clear, non-yellowing bond line.
TYPICAL CURING PERFORMANCE

Cure speed

The graph below shows the shear strength developed over time
on abraded, acid etched aluminum lap shears with an average
bondline gap of 3 to 9 mils and tested according to ASTM D1002.
GENERAL INFORMATION

This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Material Safety Data Sheet, (MSDS).
Directions for use


  1. For high strength structural bonds, removal of surface
    contaminates such as paint, oxide films, oils, dust, mold
    release agents and all other surface contaminates.
  2. Use gloves to minimize skin contact. DO NOT use solvents
    for cleaning hands.
  3. Dual Cartridges: To use simply insert the cartridge into the
    application gun and start the plunger into the cylinders using
    light pressure on the trigger. Next, remove the cartridge cap
    and expel a small amount of adhesive to be sure both sides
    are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end
    of the cartridge and begin dispensing the adhesive. For
    hand mixing, expel the desired amount of the adhesive and
    mix thoroughly. Mix approximately 15 seconds after uniform
    color is obtained. Bulk Containers: Mix thoroughly by
    weight or volume in the proportions specified in Properties
    of Uncured Material section. Mix vigorously approximately
    15 seconds after uniform color is obtained.
  4. For maximum bond strength, apply adhesive evenly to both
    surfaces to be joined.
  5. Application to the substrates should be made within 10
    minutes. Larger quantities and/or higher temperatures will
    reduce this working time.
  6. Join the adhesive coated surfaces and allow to cure at 25C
    (77F) for 24 hours for high strength. Heat up to 93C
    (200F), will speed curing.
  7. Keep parts from moving during cure. Contact pressure is
    necessary. Maximum shear strength is obtained with a 3-9
    mil bond line.
  8. Excess uncured adhesive can be cleaned up with ketone
    type solvents.

Storage

Product shall be ideally stored in a cool, dry location in
unopened containers at a temperature between 8C to 28C
(46F to 82F) unless otherwise labeled. Optimal storage is at
the lower half of this temperature range. To prevent
contamination of unused product, do not return any material to
its original container. For further specific shelf life information,
contact your local Technical Service Center.
Data Ranges

The data contained herein may be reported as a typical value
and/or range. Values are based on actual test data and are
verified on a periodic basis.
 
 