Loctite 601 Retaining Compound
Loctite 601 50ml Retaining Compound
- Strength : High
- Fixture Time Temperature : 25 °C
- Viscosity : 100 - 150 mPa.s (cP) Brookfield
- Key Substrates : Metal: Steel
- Color : Green
- Curing Type : Anaerobic
- Application : Retaining
LOCTITE 601 is a green, anaerobic, low viscosity, medium cure speed, dimethacrylate ester-based retaining compound suitable for a max. diametrical clearance of 0.1 mm. It is a high strength product for applications that require a permanent bond. Fixture time on steel is 25 min and service temperature from -55ºC to +150ºC. Fluorescence allows product presence to be monitored.
- 1-part product, requires no mixing
- Medium cure speed
- High strength for permanent bonds
- Low viscosity, small gap filling
- Fluoresces for presence monitoring
601 is designed for the bonding of cylindrical fitting
parts, particularly where low viscosity is required. The product
cures when confined in the absence of air between close fitting
metal surfaces and prevents loosening and leakage from shock
TYPICAL CURING PERFORMANCE
Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph
below shows the shear strength developed with time on steel
pins and collars compared to different materials and tested
according to ISO 10123.
Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The following
graph shows shear strength developed with time on steel pins
and collars at different controlled gaps and tested according to
Cure Speed vs. Temperature
The rate of cure will depend on the temperature. The graph
below shows the shear strength developed with time at
different temperatures on steel pins and collars and tested
according to ISO 10123.
Cure Speed vs. Activator
Where cure speed is unacceptably long, or large gaps are
present, applying activator to the surface will improve cure
speed. The graph below shows the shear strength developed
with time on zinc dichromate steel pins and collars using
Activator 7471™ and 7649™ and tested according to ISO
This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Safety Data Sheet (SDS).
Where aqueous washing systems are used to clean the
surfaces before bonding, it is important to check for
compatibility of the washing solution with the adhesive. In
some cases these aqueous washes can affect the cure and
performance of the adhesive.
This product is not normally recommended for use on plastics
(particularly thermoplastic materials where stress cracking of
the plastic could result). Users are recommended to confirm
compatibility of the product with such substrates.
Directions for use
- For best results, clean all surfaces (external and internal)
with a LOCTITE®
cleaning solvent and allow to dry.
- If the material is an inactive metal or the cure speed is too
slow, spray with Activator 7471™ or 7649™ and allow to
- For Slip Fitted Assemblies, apply adhesive around the
leading edge of the pin and the inside of the collar and
use a rotating motion during assembly to ensure good
- For Press Fitted Assemblies, apply adhesive thoroughly
to both bond surfaces and assemble at high press on
- For Shrink Fitted Assemblies the adhesive should be
coated onto the pin, the collar should then be heated to
create sufficient clearance for free assembly.
- Parts should not be disturbed until sufficient handling
strength is achieved.
- Apply localized heat to the assembly to approximately
250 °C. Disassemble while hot.
- Cured product can be removed with a combination of
soaking in a Loctite solvent and mechanical abrasion
such as a wire brush.
Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or
greater than 28 °C can adversely affect product properties.